ISO 13805:1999
(Main)Vitreous and porcelain enamels for aluminium — Determination of the adhesion of enamels on aluminium under the action of electrolytic solution (spall test)
Vitreous and porcelain enamels for aluminium — Determination of the adhesion of enamels on aluminium under the action of electrolytic solution (spall test)
This International Standard specifies a test method for the accelerated determination of the resistance of porcelain enamel coatings on aluminium and aluminium alloys to spalling as a result of exposure to moisture or weathering. Because spalling is caused by the lack of adhesion between the coating and the base metal, the spall test is a test of adhesion. The greater the extent of spalling in this test, the greater the likelihood that the article will spall in service.
Émaux vitrifiés déposés sur l'aluminium — Détermination de l'adhérence à l'aide d'un électrolyte (essai d'écaillage)
La présente Norme internationale spécifie une méthode d'essai pour la détermination accélérée de la résistance des revêtements émaillés déposés sur l'aluminium et les alliages d'aluminium à l'écaillage dû à l'humidité ou aux intempéries. L'écaillage résultant du manque d'adhérence entre le revêtement et le métal de base, l'essai d'écaillage est un essai d'adhésion. Plus le phénomène d'écaillage constaté au cours de l'essai effectué est important, plus le risque qu'il se reproduise en conditions réelles est grand.
General Information
Buy Standard
Standards Content (Sample)
INTERNATIONAL ISO
STANDARD 13805
First edition
1999-12-01
Vitreous and porcelain enamels for
aluminium — Determination of the adhesion
of enamels on aluminium under the action
of electrolytic solution (spall test)
Émaux vitrifiés déposés sur l'aluminium — Détermination de l'adhérence
à l'aide d'un électrolyte (essai d'écaillage)
A
Reference number
ISO 13805:1999(E)
---------------------- Page: 1 ----------------------
ISO 13805:1999(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO
member bodies). The work of preparing International Standards is normally carried out through ISO technical
committees. Each member body interested in a subject for which a technical committee has been established has
the right to be represented on that committee. International organizations, governmental and non-governmental, in
liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical
Commission (IEC) on all matters of electrotechnical standardization.
International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 3.
Draft International Standards adopted by the technical committees are circulated to the member bodies for voting.
Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote.
International Standard ISO 13805 was prepared by Technical Committee ISO/TC 107, Metallic and other inorganic
coatings.
© ISO 1999
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means, electronic
or mechanical, including photocopying and microfilm, without permission in writing from the publisher.
International Organization for Standardization
Case postale 56 • CH-1211 Genève 20 • Switzerland
Internet iso@iso.ch
Printed in Switzerland
ii
---------------------- Page: 2 ----------------------
©
ISO ISO 13805:1999(E)
Introduction
The spalling of porcelain enamelled aluminium, a defect characterized by separation of the porcelain enamel from
the aluminium base material, is caused by poor adhesion. The spall test is therefore capable of controlling the
quality of the enamelling process including the enamel formulation, the preparation of the base metal prior to
enamelling, the application and firing procedures, and the aluminium alloy selected for enamelling.
iii
---------------------- Page: 3 ----------------------
©
INTERNATIONAL STANDARD ISO ISO 13805:1999(E)
Vitreous and porcelain enamels for aluminium —
Determination of the adhesion of enamels on aluminium
under the action of electrolytic solution (spall test)
1 Scope
This International Standard specifies a test method for the accelerated determination of the resistance of porcelain
enamel coatings on aluminium and aluminium alloys to spalling as a result of exposure to moisture or weathering.
Because spalling is caused by the lack of adhesion between the coating and the base metal, the spall test is a test
of adhesion. The greater the extent of spalling in this test, the greater the likelihood that the article will spall in
service.
2 Normative references
The following normative documents contain provisions which, through reference in this text, constitute provisions of
this International Standard. For dated references, subsequent amendments to, or revisions of, any of these
publications do not apply. However, parties to agreements based on this International Standard are encouraged to
investigate the possibility of applying the most recent editions of the normative document indicated below. For
undated references, the latest edition of normative document referred to applies. Members of ISO and IEC maintain
registers of currently valid International Standards.
IS0 3819, Laboratory glassware — Beakers.
ISO 4788, Laboratory glassware — Graduated measuring cylinders.
ISO 10141, Vitreous and porcelain enamels — Vocabulary.
ISO 13805, Vitreous and porcelain enamels on aluminium — Production of specimens for testing.
3 Terms and definitions
For the purposes of this International Standard, the terms and definitions given in ISO 10141 apply.
4 Principle
A scored enamelled aluminium specimen is exposed to an aqueous test solution consisting of antimony trichloride,
O O
SbCl , having a concentration
...
NORME ISO
INTERNATIONALE 13805
Première édition
1999-12-01
Émaux vitrifiés déposés sur l'aluminium —
Détermination de l'adhérence à l'aide d'un
électrolyte (essai d'écaillage)
Vitreous and porcelain enamels for aluminium — Determination of the
adhesion of enamels on aluminium under the action of electrolytic solution
(spall test)
A
Numéro de référence
ISO 13805:1999(F)
---------------------- Page: 1 ----------------------
ISO 13805:1999(F)
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes nationaux de
normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est en général confiée aux
comités techniques de l'ISO. Chaque comité membre intéressé par une étude a le droit de faire partie du comité
technique créé à cet effet. Les organisations internationales, gouvernementales et non gouvernementales, en
liaison avec l'ISO participent également aux travaux. L'ISO collabore étroitement avec la Commission
électrotechnique internationale (CEI) en ce qui concerne la normalisation électrotechnique.
Les Normes internationales sont rédigées conformément aux règles données dans les Directives ISO/CEI, Partie 3.
Les projets de Normes internationales adoptés par les comités techniques sont soumis aux comités membres pour
vote. Leur publication comme Normes internationales requiert l'approbation de 75 % au moins des comités
membres votants.
La Norme internationale ISO 13805 a été élaborée par le comité technique ISO/TC 107, Revêtements métalliques
et autres revêtements inorganiques.
© ISO 1999
Droits de reproduction réservés. Sauf prescription différente, aucune partie de cette publication ne peut être reproduite ni utilisée sous quelque
forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie et les microfilms, sans l'accord écrit de l'éditeur.
Organisation internationale de normalisation
Case postale 56 • CH-1211 Genève 20 • Suisse
Internet iso@iso.ch
Imprimé en Suisse
ii
---------------------- Page: 2 ----------------------
©
ISO ISO 13805:1999(F)
Introduction
L'écaillage de l'aluminium émaillé, c'est-à-dire un défaut caractérisé par la séparation de l'émail et du matériau de
base en aluminium, résulte d'un manque d'adhérence. L'essai d'écaillage permet ainsi de contrôler la qualité du
procédé d'émaillage, y compris la formulation de l'émail, la préparation du matériau de base avant l'émaillage, les
modes opératoires de cuisson et d'application et l'alliage d'aluminium choisi pour l'émaillage.
iii
---------------------- Page: 3 ----------------------
©
NORME INTERNATIONALE ISO ISO 13805:1999(F)
Émaux vitrifiés déposés sur l'aluminium — Détermination
de l'adhérence à l'aide d'un électrolyte (essai d'écaillage)
1 Domaine d'application
La présente Norme internationale spécifie une méthode d'essai pour la détermination accélérée de la résistance
des revêtements émaillés déposés sur l'aluminium et les alliages d'aluminium à l'écaillage dû à l'humidité ou aux
intempéries. L'écaillage résultant du manque d'adhérence entre le revêtement et le métal de base, l'essai
d'écaillage est un essai d'adhésion. Plus le phénomène d'écaillage constaté au cours de l'essai effectué est
important, plus le risque qu'il se reproduise en conditions réelles est grand.
2 Références normatives
Les documents normatifs suivants contiennent des dispositions qui, par suite de la référence qui y est faite,
constituent des dispositions valables pour la présente Norme internationale. Pour les références datées, les
amendements ultérieurs ou les révisions de ces publications ne s’appliquent pas. Toutefois, les parties prenantes
aux accords fondés sur la présente Norme internationale sont invitées à rechercher la possibilité d'appliquer les
éditions les plus récentes des documents normatifs indiqués ci-après. Pour les références non datées, la dernière
édition du document normatif en référence s’applique. Les membres de l'ISO et de la CEI possèdent le registre des
Normes internationales en vigueur.
ISO 3819, Verrerie de laboratoire — Béchers.
ISO 4788, Verrerie de laboratoire — Éprouvettes graduées cylindriques.
ISO 10141, Émaux vitrifiés sur l’aluminium — Vocabulaire.
ISO 13804, Émaux vitrifiés déposés sur l’aluminium — Fabrication des échantillons pour essais.
3 Termes et définitions
Pour les besoins de la présente Norme internationale, les termes et définitions donnés dans l’ISO 10141
s'appliquent.
4 Principe
Un échantillon émaillé d'aluminium rayé est plongé dans une solution d'essai aqueuse composée de chlorure
d'antimoine (SbCl ), avec une concentration de 10 g/l à une température ambiante comprise entre 18 °C et 28 °C,
3
pendant 20 h.
1
---------------------- Page: 4 ----------------------
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.